Influência da termociclagem na resistência de união de raízes restauradas com MTA e pino de fibra

Silva, Jessica Penha Verçosa e

Use este identificador para citar ou linkar para este item: http://repositorioinstitucional.uea.edu.br//handle/riuea/746

Registro completo de metadados

Campo DC	Valor	Idioma
dc.contributor.author	Silva, Jessica Penha Verçosa e	-
dc.date.available	2017-12-07T13:08:56Z	-
dc.date.issued	2017-12-06	-
dc.identifier.uri	http://repositorioinstitucional.uea.edu.br/handle/riuea/746	-
dc.description	Estabelecer a resistência de união adequada entre o pino de fibra e o dente é de extrema importância para um bom prognostico do tratamento. Dentes fragilizados pelo tratamento endodôntico podem sofrer maiores danos ao serem perfurados. Após fazer o selamento desta perfuração com MTA, há um questionamento quanto à influência deste à resistência de união, além de ao agregarmos um fator de estresse no conjunto pino, cimento e MTA, qual seria o efeito. Assim, o objetivo deste estudo foi avaliar a influência da termociclagem na resistência de união de raízes endodonticamente tratadas e restauradas com trióxido mineral agregado (MTA) em perfurações de 1,0mm na dentina radicular e pinos de fibra de vidro intrarradicular. Foram selecionados 20 dentes bovinos, que tiveram suas coroas cortadas e realizado o tratamento endodôntico do conduto. Foram feitas perfurações laterais de 1,0mm de diâmetro nos terços cervical, médio e apical, seladas com MTA. Em seguida, os condutos foram preparados para cimentação de pino de fibra de vidro com cimento resinoso autoadesivo. Separou-se as amostras randomicamente, em grupo controle (sem termociclagem) e grupo teste (com termociclagem), cujas amostras passaram por 5.000 ciclos em temperaturas de 5ºC, 37ºC e 55ºC. Logo após, os dois grupos foram mantidos em solução de azul de metileno 2%, por 24h, em estufa com 37ºC. Os espécimes foram seccionados nos três terços radiculares do pino, com 3,0mm de espessura e foram levados à Máquina de Ensaios Universal para teste de resistência ao cisalhamento ´´push-out´´. Depois foi avaliado o grau de infiltração de umidade nas perfurações restauradas com MTA, por meio da percolação do corante. A análise dos resultados foi feita com o teste ANOVA e Teste de Tukey (p<0,05). Após análise, verificou-se que o grupo teste apresentava maiores valores resistências nos terços cervical e médio, onde se pode afirmar que houve influência da termociclagem e quanto ao grau de infiltração houve bom selamento das restaurações com MTA.	pt_BR
dc.description.abstract	Establishing the proper bond strength between the fiber pin and the tooth is of utmost importance for a good prognosis of the treatment. Teeth weakened by endodontic treatment may suffer greater damage when pierced. After the sealing of this drilling with MTA, there is a question about the influence of this to the bond strength, besides adding a stress factor in the pin, cement and MTA, what would be the effect. Thus, the objective of this study was to evaluate the influence of thermocycling on the bond strength of endodontically treated and restored roots with aggregated mineral trioxide (MTA) in 1.0 mm perforations in root dentin and intrarradicular fiberglass pins. Twenty bovine teeth were selected, which had their crowns cut and the endodontic treatment of the conduit was performed. Lateral perforations of 1.0mm diameter were made in the cervical, middle and apical thirds, sealed with MTA. Then, the conduits were prepared for fiberglass pin cementation with self-adhesive resin cement. Samples were randomly divided into a control group (without thermocycling) and a test group (with thermocycling), whose samples went through 5,000 cycles at temperatures of 5 ° C, 37 ° C and 55 ° C. Soon after, the two groups were kept in 2% methylene blue solution for 24 hours in a 37ºC oven. The specimens were sectioned into the three-thirds root of the pin, 3.0mm thick and were taken to the Universal Testing Machine for 'push-out' shear strength test. Then, the degree of moisture infiltration in the restorations with MTA was evaluated by means of percolation of the dye. The analysis of the results was done with ANOVA and Tukey's test (p <0.05). After analysis, it was verified that the test group presented higher resistance values in the cervical and middle thirds, where it can be affirmed that there was influence of the thermocycling and as to the degree of infiltration there was good sealing of the restorations with MTA.	pt_BR
dc.language.iso	por	pt_BR
dc.publisher	Universidade do Estado do Amazonas	pt_BR
dc.rights	Attribution-NonCommercial-NoDerivs 3.0 Brazil	*
dc.rights.uri	http://creativecommons.org/licenses/by-nc-nd/3.0/br/	*
dc.subject	Retentor intra-radicular	pt_BR
dc.subject	Cimentos de resina	pt_BR
dc.subject	materiais restauradores	pt_BR
dc.subject	Canal radicular	pt_BR
dc.title	Influência da termociclagem na resistência de união de raízes restauradas com MTA e pino de fibra	pt_BR
dc.title.alternative	Influence of thermocycling on the bond strength of roots restored with MTA and fiber pine	pt_BR
dc.type	Trabalho de Conclusão de Curso	pt_BR
dc.date.accessioned	2017-12-07T13:08:56Z	-
Aparece nas coleções:	ESA - Trabalho de Conclusão de Curso Graduação

Arquivos associados a este item:

Arquivo	Descrição	Tamanho	Formato
Influência da termociclagem na resistência de união de raízes restauradas com MTA e pino de fibra.pdf		1,32 MB	Adobe PDF	Visualizar/Abrir

Mostrar registro simples do item Visualizar estatísticas

Este item está licenciada sob uma Licença Creative Commons